Our Engineering SLA Resin – Tough is extremely transparent. It perfectly balances a high impact strength with semi-flexibility.

Its high level of toughness makes this resin ideal for creating strong and functional parts that will be exposed to repeated brief periods of intense stress or strain

Key features

• High impact resistance
• Good UV and weather resistance
• Good fatigue resistance
• Extremely transparent with virtually no discoloration and/or yellowing
• High dimensional accuracy and low shrinkage
• Almost odorless processing
• Compatible with all open-source SLA, DLP, and LCD 3D printers in the range of 385 – 405nm

Applications

• Snap-fit assemblies
• Tooling
• Functional prototyping
• Protective cases
• Outdoor parts
• Short-run manufacturing

Resin properties (uncured liquid)

• Viscosity: 1000 cps at 25°C
• Density: 1.12 g/cm2

Mechanical properties

Test method on post cured objects through 10 minutes high power mercury curing.

Please note that the above-displayed values can vary with individual machine processing, post-curing parts,  geometry, print orientation, print settings, and temperature.

Preparation(s) before starting to print

• Shake the bottle for at least 2 minutes before each use.
• After shaking the bottle, leave the resin to rest for 10 minutes to let air bubbles get out of the resin
• The resin can be poured back from the vat into the bottle once your print is finished
• Always use protective measurements like safety glasses and nitrile gloves when handling resins.

Anycubic Photon Mono SE

50µm
First / Burn-in Layers: 4x to 6x for 65 to 70 Seconds
Normal Layers: 7.5 to 8.5 Seconds
Lifting Distance: 6mm
Light-off Delay: 1
Bottom Light-off Delay: 3

Elegoo Mars 2 / Pro

50µm
First / Burn-in Layers: 4x to 6x for 75 Seconds
Normal Layers: 8 to 10 Seconds
Lifting Distance: 6mm
Light-off Delay: 1
Bottom Light-off Delay: 3

Post-processing

• We do advise you to post-process your 3D print in order to achieve the material properties
• Rinse your 3D printed object in IPA or (Bio)Ethanol for approximately 5 minutes
• An ultrasonic cleaner is preferred/recommended
• Make sure that IPA and/or (Bio)Ethanol rinsed objects are perfectly dry before further post-curing
• Place the rinsed parts in a well-ventilated area for at least 30 minutes, or use pressurized air for at least 2 minutes
• Cure your object in a high power curing chamber for approximately 20-30 minutes at 65° C
• The preferred curing wavelength is between 300-410nm

Safety

Please always be aware that when 3D printing with resins that you are working with chemicals and that you should always be cautious and use the personal protective equipment as stipulated in our safety data sheets.

• Always wear Respiratory Protection when sanding/cutting the resin object.
• Always use nitrile gloves when handling resins and uncured resin objects.